Overview of materials for Ethylene Butyl Acrylate

Category Polymer , Thermoplastic , Ethylene Butyl Acrylate
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Ethylene Butyl Acrylate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Butyl Acrylate". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.895 - 1.48 g/cc
0.0323 - 0.0535 lb/in³
Average value: 0.986 g/cc Grade Count:93
Viscosity 8300 - 8340 cP

@Temperature 190 - 190 °C
8300 - 8340 cP

@Temperature 374 - 374 °F
Average value: 8320 cP Grade Count:2
Butyl Acrylate Content 6.00 - 37.0 %
6.00 - 37.0 %
Average value: 25.2 % Grade Count:14
Thickness 25.0 - 40.0 microns
0.984 - 1.57 mil
Average value: 35.0 microns Grade Count:3
Melt Flow 0.250 - 900 g/10 min
0.250 - 900 g/10 min
Average value: 34.2 g/10 min Grade Count:84
Mechanical Properties Metric English Comments
Hardness, Shore A 44.0 - 90.0
44.0 - 90.0
Average value: 71.1 Grade Count:20
Hardness, Shore D 23.0 - 80.0
23.0 - 80.0
Average value: 43.8 Grade Count:18
Tensile Strength, Ultimate 0.965 - 31.0 MPa
140 - 4500 psi
Average value: 13.9 MPa Grade Count:62
Tensile Strength, Yield 3.50 - 38.0 MPa
508 - 5510 psi
Average value: 22.1 MPa Grade Count:57
Film Elongation at Break, MD 200 - 240 %
200 - 240 %
Average value: 213 % Grade Count:3
Film Elongation at Break, TD 600 - 680 %
600 - 680 %
Average value: 627 % Grade Count:3
Elongation at Break 4.00 - 1210 %
4.00 - 1210 %
Average value: 340 % Grade Count:64
Elongation at Yield 2.30 - 14.5 %
2.30 - 14.5 %
Average value: 5.52 % Grade Count:42
Modulus of Elasticity 0.0250 - 4.50 GPa
3.63 - 653 ksi
Average value: 1.69 GPa Grade Count:45
Flexural Modulus 0.00538 - 4.35 GPa
0.780 - 631 ksi
Average value: 1.49 GPa Grade Count:35
Izod Impact Unnotched 4.20304 - 4.20304 J

@Temperature -17.8 - -17.8 °C
3.10000 - 3.10000 ft-lb

@Temperature 0.000 - 0.000 °F
Average value: 4.20 J Grade Count:1
Izod Impact, Notched (ISO) 3.15 - 52.5 kJ/m²
1.50 - 25.0 ft-lb/in²
Average value: 34.3 kJ/m² Grade Count:7
Charpy Impact Unnotched 2.31 - 10.1 J/cm²
11.0 - 48.0 ft-lb/in²
Average value: 5.32 J/cm² Grade Count:3
1.596 - 2.10 J/cm²

@Temperature -30.0 - 0.000 °C
7.596 - 9.99 ft-lb/in²

@Temperature -22.0 - 32.0 °F
Average value: 1.85 J/cm² Grade Count:1
Charpy Impact, Notched 0.231 - 6.51 J/cm²
1.10 - 31.0 ft-lb/in²
Average value: 1.42 J/cm² Grade Count:38
0.1302 - 1.491 J/cm²

@Temperature -30.0 - 0.000 °C
0.6197 - 7.096 ft-lb/in²

@Temperature -22.0 - 32.0 °F
Average value: 0.606 J/cm² Grade Count:28
Gardner Impact 8.83543 - 8.83543 J

@Temperature -28.9 - -28.9 °C
6.51667 - 6.51667 ft-lb

@Temperature -20.0 - -20.0 °F
Average value: 8.84 J Grade Count:1
8.83543 - 8.83543 J

@Thickness 3.17 - 3.17 mm
6.51667 - 6.51667 ft-lb

@Thickness 0.125 - 0.125 in
Average value: 8.84 J Grade Count:1
Dart Drop, Total Energy 24.9471 - 29.0145 J

@Temperature -30.0 - -15.0 °C
18.4000 - 21.4000 ft-lb

@Temperature -22.0 - 5.00 °F
Average value: 26.3 J Grade Count:5
26.1673 - 26.1673 J

@Temperature -30.0 - -30.0 °C
19.3000 - 19.3000 ft-lb

@Temperature -22.0 - -22.0 °F
Average value: 26.3 J Grade Count:1
26.1673 - 26.1673 J

@Thickness 3.20 - 3.20 mm
19.3000 - 19.3000 ft-lb

@Thickness 0.126 - 0.126 in
Average value: 26.3 J Grade Count:1
Coefficient of Friction 0.100 - 0.450
0.100 - 0.450
Average value: 0.233 Grade Count:3
Film Tensile Strength at Break, MD 24.0 - 25.0 MPa
3480 - 3630 psi
Average value: 24.3 MPa Grade Count:3
Film Tensile Strength at Break, TD 15.0 - 18.0 MPa
2180 - 2610 psi
Average value: 17.0 MPa Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 0.504 - 0.774 µm/m-°C
0.280 - 0.430 µin/in-°F
Average value: 0.583 µm/m-°C Grade Count:5
Melting Point -75.0 - 143 °C
-103 - 289 °F
Average value: 74.6 °C Grade Count:34
Deflection Temperature at 0.46 MPa (66 psi) 68.9 - 142 °C
156 - 288 °F
Average value: 104 °C Grade Count:30
Deflection Temperature at 1.8 MPa (264 psi) 43.9 - 92.8 °C
111 - 199 °F
Average value: 57.1 °C Grade Count:47
Vicat Softening Point 40.0 - 153 °C
104 - 307 °F
Average value: 63.7 °C Grade Count:20
Brittleness Temperature -73.0 - -30.0 °C
-99.4 - -22.0 °F
Average value: -62.3 °C Grade Count:4
Glass Transition Temp, Tg -55.0 - -50.0 °C
-67.0 - -58.0 °F
Average value: -53.9 °C Grade Count:9
Ring & Ball Softening Point 55.0 - 190 °C
131 - 374 °F
Average value: 107 °C Grade Count:5
Electrical Properties Metric English Comments
Electrical Resistivity 25.0 - 1.00e+16 ohm-cm
25.0 - 1.00e+16 ohm-cm
Average value: 2.95e+15 ohm-cm Grade Count:4
40.0 - 3.60e+14 ohm-cm

@Temperature 70.0 - 90.0 °C
40.0 - 3.60e+14 ohm-cm

@Temperature 158 - 194 °F
Average value: 1.90e+14 ohm-cm Grade Count:3
Surface Resistance 1.70e+14 - 4.80e+14 ohm

@Temperature 70.0 - 70.0 °C
1.70e+14 - 4.80e+14 ohm

@Temperature 158 - 158 °F
Average value: 3.25e+14 ohm Grade Count:2
Dielectric Constant 2.70 - 6.10
2.70 - 6.10
Average value: 4.28 Grade Count:3
Dissipation Factor 0.00100 - 0.133
0.00100 - 0.133
Average value: 0.0462 Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 160 - 300 °C
320 - 572 °F
Average value: 221 °C Grade Count:12
Adapter Temperature 180 - 290 °C
356 - 554 °F
Average value: 240 °C Grade Count:6
Die Temperature 141 - 290 °C
285 - 554 °F
Average value: 235 °C Grade Count:7
Melt Temperature 115 - 290 °C
239 - 554 °F
Average value: 191 °C Grade Count:12