SABIC Innovative Plastics Valox® 451E PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 451E PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% GR. Easy flow version of VALOX 451.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0060 - 0.0090 cm/cm @Thickness 3.20 - 4.60 mm |
0.0060 - 0.0090 in/in @Thickness 0.126 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm @Thickness 1.50 - 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0080 - 0.011 cm/cm @Thickness 3.20 - 4.60 mm |
0.0080 - 0.011 in/in @Thickness 0.126 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 151 MPa | 21900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.51 GPa | 799 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 6.40 mm |
414 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C @Thickness 6.40 mm |
385 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.710 mm |
V-0 @Thickness 0.0280 in |
UL 94 |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.65cm^3/g | ASTM D792 |
Users viewing this material also viewed the following:
- KaMin Polyfil® HG Kaolin Clay - Waterwashed
- Teknor Apex APEX® 4107 Polyvinyl Chloride, Flexible
- PlastxWorld Veroplas PA5300 Nylon 6
- Polyram PlusTek RA325J5 Nylon 6.6, 25% Glass beads and Glass Fiber, Flame Retardant
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Non-Black, Hi-Sil 233
- Covestro Apec® 2095 Polycarbonate
- Colorite Polymers 1066 Non-Phthalate 66 Series Vinyl Compound
- BNZ Materials Transite HT Low Temperature Industrial Board
- DuPont Bynel® 50E631 Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved