SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D 792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.90 % @Temperature 23.0 °C |
0.90 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | on tensile bar; SABIC Method |
| 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 6.60 kg, Temperature 295 °C |
8.0 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D 1238 |
| 40 g/10 min @Load 5.00 kg, Temperature 340 °C |
40 g/10 min @Load 11.0 lb, Temperature 644 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 66 g/10 min @Load 6.60 kg, Temperature 337 °C |
66 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D 638 |
| 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D 638 |
| 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 20 % | 20 % | Type I, 5 mm/min; ASTM D 638 |
| 27 % | 27 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.7 % | 6.7 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.90 GPa | 421 ksi | 5 mm/min; ASTM D 638 |
| 3.08 GPa | 447 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 138 MPa | 20000 psi | 2 mm/min; ISO 178 |
| 146 MPa | 21200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.95 GPa | 428 ksi | 2 mm/min; ISO 178 |
| 3.20 GPa | 464 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.450 J/cm @Temperature -30.0 °C |
0.843 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| 15.0 J/cm @Thickness 3.20 mm |
28.1 ft-lb/in @Thickness 0.126 in |
reverse notched; ASTM D 256 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 125 kJ/m² @Temperature -30.0 °C |
59.5 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| 131 kJ/m² @Temperature 23.0 °C |
62.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 11.5 J/cm² @Temperature -30.0 °C |
54.7 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 18.0 J/cm² @Temperature 23.0 °C |
85.7 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 35.0 J @Temperature 23.0 °C |
25.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 53.0 µm/m-°C @Temperature -40.0 - 150 °C |
29.4 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 53.0 µm/m-°C @Temperature 23.0 - 150 °C |
29.4 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature -40.0 - 150 °C |
29.4 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 53.0 µm/m-°C @Temperature 23.0 - 150 °C |
29.4 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 180 °C @Thickness 3.20 mm |
356 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 186 °C @Thickness 6.40 mm |
367 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 192 °C | 378 °F | Rate B/50; ISO 306 |
| 201 °C | 394 °F | Rate B/120; ISO 306 | |
| 201 °C | 394 °F | Rate B/50; ASTM D 1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3885H TPE, PP Overmold or Standalone use
- Styron CALIBREâ„¢ 5101-15 Polycarbonate Resin
- SABIC Innovative Plastics LNP THERMOCOMP ZFM62P PPE+PS
- A. Schulman POLYFORT™ FPP 1453 Calcium Carbonate Filled Homopolymer Polypropylene
- ExxonMobil Exceed™ 2018EB Metallocene Polyethylene Resin (European Grade)
- 3M Scotchcal™ 3632-87 Translucent Film
- 3M Scotchcast™ 265 Electrical Epoxy Powder Resin
- ITW Plexus Plexus™ MA925 Methacrylate Adhesive
- Taiwan Sheen Soon Sheenthane® A9830 Thermoplastic Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved