- Eurostar Staramide AK6 PA66, 30% Mineral Reinforced, Injection Molding
Eurostar Staramide AK6 PA66, 30% Mineral Reinforced, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide AK6 PA66, 30% Mineral Reinforced, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide AK6 is a 30% Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm | 0.010 - 0.014 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.50 GPa | 798 ksi | 1 mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 400 µm/m-°C @Temperature 23.0 - 80.0 °C |
222 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 255 °C | 491 °F | B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 2815 HDPE Injection Molding Resin
- Nilit FRIANYL B63 W-SG30 Nylon 6 for injection molding, 30% mineral filled
- ICO Polymers ICORENEâ„¢ 190-3561 LMDPE Rotational Molding Resin
- Universal Wire Works 410 Stainless Steel Electrode
- Zotefoams Evazote® EV50 Ethylene Vinyl Acetate Copolymer Foam
- Total PPC 4820WZ Polypropylene, Impact Copolymer
- Aremco HiE-Coat™ 840-MS High Emissivity Coating, Silicone-Ceramic Filled
- BASF Ultramid® A3EG3 15% Glass Filled PA66 (Conditioned)
- EMS-Griltech Grilon® BA 3100 White Nylon 66/Nylon 6 Bi-Component Fiber
Copyright © lookpolymers.com All Rights Reserved