Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | ULTEM |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics Ultem ATX100F PEI (Europe-Africa-Middle East).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C / 50% RH; ISO 62 |
Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
ISO 62 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
Melt Flow | 35 g/10 min @Load 5.00 kg, Temperature 340 °C |
35 g/10 min @Load 11.0 lb, Temperature 644 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, H358/30 | 95.0 MPa | 13800 psi | ISO 2039-1 |
Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
Elongation at Break | 30 % | 30 % | 50 mm/min; ISO 527 |
Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
Tensile Modulus | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
1.90 J/cm² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 23.0 - 150 °C |
33.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 23.0 - 150 °C |
33.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ISO 8302 |
Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
Vicat Softening Point | 170 °C | 338 °F | Rate B/50; ISO 306 |
175 °C | 347 °F | Rate B/120; ISO 306 | |
180 °C | 356 °F | Rate A/50; ISO 306 | |
Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 by SABIC-IP |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
2.9 @Frequency 50.0 - 60.0 Hz |
2.9 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
Dielectric Strength | 22.0 kV/mm @Thickness 3.20 mm |
559 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz |
0.0010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
IEC 60250 | |
Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
Descriptive Properties | Value | Comments |
---|---|---|
Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |