SABIC Innovative Plastics ULTEM 2310 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 2310 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.6 g/10 min @Load 6.60 kg, Temperature 337 °C |
7.6 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 168 MPa | 24400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 9.23 GPa | 1340 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 220 MPa | 31900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 9.23 GPa | 1340 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| 4.37 J/cm @Thickness 3.20 mm |
8.19 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.2 µm/m-°C @Temperature -20.0 - 150 °C |
9.00 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 41.4 µm/m-°C @Temperature -20.0 - 150 °C |
23.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 180 °C | 356 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 180 °C | 356 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.250 mm |
V-0 @Thickness 0.00984 in |
UL 94 |
| 5VA @Thickness 1.21 mm |
5VA @Thickness 0.0476 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 51 T 60 PP, 60% mineral filling
- Plastcom SLOVAMID 6 LI/1 Polyamide 6, Impacted
- Fainplast Compounds RH 211/W Rigid PVC, Antishock Extrusion
- Taiwan Sheen Soon Sheenthane® A8970A Film Grade Thermoplastic Polyurethane Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP HX03408 PA11
- Chase Plastics CP Pryme® A100HF ABS Molding Resin, High Flow
- American Elements Samarium Oxide Nanopowder
- UBE UBEPOL BR150B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Axiall 3650 Rigid PVC, Extrusion
- Overview of materials for Polypropylene, Long Glass Fiber 50%
Copyright © lookpolymers.com All Rights Reserved