SABIC Innovative Plastics ULTEM 2300R PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 2300R PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Physical Properties Metric English Comments
Specific Gravity 1.51 g/cc
1.51 g/cc
ASTM D792
Water Absorption 0.16 %

@Time 86400 sec
 0.16 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 0.90 %
0.90 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 5.3 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 5.3 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 114
114
ASTM D785
Tensile Strength at Break 158 MPa
22900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 168 MPa
24400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 9.30 GPa
1350 ksi
5 mm/min; ASTM D638
Flexural Strength 227 MPa
32900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 8.96 GPa
1300 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
4.91 J/cm

@Thickness 3.20 mm
 9.20 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Izod Impact, Unnotched 4.27 J/cm
8.00 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.8 µm/m-°C

@Temperature -20.0 - 150 °C
 11.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 212 °C

@Thickness 6.40 mm
 414 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 227 °C
441 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 180 °C
356 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 180 °C
356 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.250 mm
 V-0

@Thickness 0.00984 in
 UL 94
5VA

@Thickness 1.21 mm
 5VA

@Thickness 0.0476 in
 UL 94
Oxygen Index 50 %
50 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+16 ohm-cm
3.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.7

@Frequency 1000 Hz
 3.7

@Frequency 1000 Hz
 ASTM D150
Dielectric Strength 24.8 kV/mm

@Thickness 1.60 mm
 630 kV/in

@Thickness 0.0630 in
 in air; ASTM D149
30.3 kV/mm

@Thickness 1.60 mm
 770 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
Dissipation Factor 0.0015

@Frequency 1000 Hz
 0.0015

@Frequency 1000 Hz
 ASTM D150
0.0053

@Frequency 2.45e+9 Hz
 0.0053

@Frequency 2.45e+9 Hz
 ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
NBS Smoke Density, Flaming, Ds 4 min 1.6
ASTM E 662