SABIC Innovative Plastics ULTEM 2210EPR PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 2210EPR PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing.
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 13 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 13 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 137 MPa
19900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 137 MPa
19900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 6.89 GPa
999 ksi
5 mm/min; ASTM D638
Flexural Strength 206 MPa
29900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Yield Strength 206 MPa
29900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 6.89 GPa
999 ksi
1.3 mm/min, 50 mm span; ASTM D790
6.89 GPa
999 ksi
2.6 mm/min, 100 mm span; ASTM D790
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.87 J/cm
11.0 ft-lb/in
ASTM D4812
Dart Drop, Total Energy 14.0 J

@Temperature 23.0 °C
 10.3 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 211 °C

@Thickness 3.20 mm
 412 °F

@Thickness 0.126 in
 unannealed; ASTM D648
213 °C

@Thickness 6.40 mm
 415 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 206 °C

@Thickness 3.20 mm
 403 °F

@Thickness 0.126 in
 unannealed; ASTM D648
208 °C

@Thickness 6.40 mm
 406 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 210 °C
410 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 UL 94
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A