DuPont Performance Polymers Rynite® FR530L BK507 Polyethylene Terephthalate (PET)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Rynite® FR530L BK507 Polyethylene Terephthalate (PET).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Rynite FR530 BK507 is a 30% glass reinforced flame retardant modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
| Elongation at Break | 1.9 % | 1.9 % | ISO 527-1/-2 |
| Tensile Modulus | 11.3 GPa | 1640 ksi | ISO 527-1/-2 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| 3.00 J/cm² @Temperature -40.0 °C |
14.3 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| 0.800 J/cm² @Temperature -40.0 °C |
3.81 ft-lb/in² @Temperature -40.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C | 7.78 µin/in-°F | ISO 11359-1/-2 |
| 20.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
11.1 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| 73.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
40.6 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
| Melting Point | 252 °C | 486 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 243 °C | 469 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| UL RTI, Electrical | 155 °C @Thickness 0.400 mm |
311 °F @Thickness 0.0157 in |
UL 746B |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
IEC 60695-11-10 |
| V-0 @Thickness 0.300 mm |
V-0 @Thickness 0.0118 in |
IEC 60695-11-10 | |
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
IEC 60695-11-20 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 |
| 250 - 400 V | 250 - 400 V | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Part Marking Code | >PET-GF30FR< | ISO 11469 |
| Processing | Injection Moulding | |
| Regional Availability | Europe | |
| Near East/Africa | ||
| Resin Identification | PET-GF30FR(17) | |
| UL recognition | UL |
Users viewing this material also viewed the following:
- Ineos ABS Lustran® 743 General Purpose, High-Impact (discontinued **)
- Lubriplate Super GPO L0754 Heavy-Duty Motor Oil Motor Oil & Transmission Fluid
- Indium Corp. Indalloy 51E Low Melting Gallium Alloy
- Saint-Gobain Rulon® 1045 Bearing/Seal PTFE
- Teknor Apex Telcar® TL-1183A Thermoplastic Elastomer
- Teknor Apex Telcar® TL-2588L Thermoplastic Elastomer
- ELASTO UK Dryflex® 600300S SEBS Based Material, Filled Qualities, 30A Hardness, Natural
- Ensinger Tecatron® XP-170 Compression Molded PPS Compound, EWS Filled
Copyright © lookpolymers.com All Rights Reserved