Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
Moisture Absorption at Equilibrium | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ASTM D 570 |
Water Absorption at Saturation | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ISO 62 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 120 | 120 | ASTM D 785 |
120 | 120 | ISO 2039-2 | |
Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 |
63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
Elongation at Break | >= 70 % | >= 70 % | Type I, 50 mm/min; ASTM D 638 |
>= 70 % | >= 70 % | 50 mm/min; ISO 527 | |
Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 |
6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
Tensile Modulus | 2.35 GPa | 341 ksi | 50 mm/min; ASTM D 638 |
2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
2.30 GPa | 334 ksi | 2 mm/min; ISO 178 | |
Izod Impact, Notched | 9.00 J/cm @Temperature 23.0 °C |
16.9 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
Impact Test | 65.0 J @Temperature 23.0 °C |
47.9 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C 177 |
0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 | |
Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
ASTM D 648 | |
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
ASTM D 648 | |
Vicat Softening Point | 144 °C | 291 °F | Rate B/50; ASTM D 1525 |
144 °C | 291 °F | Rate B/50; ISO 306 |
Optical Properties | Metric | English | Comments |
---|---|---|---|
Refractive Index | 1.586 | 1.586 | ASTM D 542 |
1.586 | 1.586 | ISO 489 | |
Haze | <= 0.80 % @Thickness 2.54 mm |
<= 0.80 % @Thickness 0.100 in |
ASTM D 1003 |
Transmission, Visible | 88 - 90 % @Thickness 2.54 mm |
88 - 90 % @Thickness 0.100 in |
ASTM D 1003 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D 257 |
>= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | |
Dielectric Constant | 3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
ASTM D 150 |
3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D 150 | |
3.0 @Frequency 60.0 Hz |
3.0 @Frequency 60.0 Hz |
IEC 60250 | |
3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |
Dielectric Strength | 27.0 kV/mm @Thickness 1.60 mm |
686 kV/in @Thickness 0.0630 in |
ASTM D 149 |
27.0 kV/mm @Thickness 1.60 mm |
686 kV/in @Thickness 0.0630 in |
IEC 60243-1 | |
Dissipation Factor | 0.0010 @Frequency 60.0 Hz |
0.0010 @Frequency 60.0 Hz |
ASTM D 150 |
0.0010 @Frequency 60.0 Hz |
0.0010 @Frequency 60.0 Hz |
IEC 60250 | |
0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 | |
0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
ASTM D 150 |
Descriptive Properties | Value | Comments |
---|---|---|
Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |