SABIC Innovative Plastics Noryl PPX PPX615 PPE+PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl PPX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl PPX PPX615 PPE+PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good chemical resistance. Designed for a balance of stiffness and practical impact strength.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D 792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.030 % | 0.030 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.040 % @Temperature 23.0 °C |
0.040 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | on tensile bar; SABIC Method |
| 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 4.4 g/10 min @Load 5.00 kg, Temperature 260 °C |
4.4 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| 5.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D 638 |
| 59.0 MPa | 8560 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 5 mm/min; ASTM D 638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.2 % | 4.2 % | 5 mm/min; ISO 527 |
| 4.3 % | 4.3 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.49 GPa | 506 ksi | 5 mm/min; ASTM D 638 |
| 4.04 GPa | 586 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.06 GPa | 444 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 3.53 GPa | 512 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature -30.0 °C |
1.20 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 1.07 J/cm @Temperature 23.0 °C |
2.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 5.82 J/cm @Temperature 23.0 °C |
10.9 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² @Temperature -30.0 °C |
18.1 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| 42.0 kJ/m² @Temperature 23.0 °C |
20.0 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.10 J/cm² @Temperature -30.0 °C |
19.5 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 5.10 J/cm² @Temperature 23.0 °C |
24.3 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 49.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 49.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 98.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 98.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 150 °C @Thickness 3.20 mm |
302 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 123 °C | 253 °F | Rate B/50; ASTM D 1525 |
| 123 °C | 253 °F | Rate B/50; ISO 306 | |
| 124 °C | 255 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 41 HF General Purpose Acrylic Resin
- Polimeri Europa Sinkral® C 442 ABS Resin
- Mitsui Fybrel® E 620 Polyolefin Synthetic Pulp, Wet Processes (discontinued **)
- Ineos Nova 3601 General Purpose Crystal Polystyrene (discontinued **)
- Overview of materials for Polypropylene, Fiber Grade
- Johnson Matthey JM A25 Soft Solder/Flux
- Multibase Multi-ABS 7522 R , 22% Filler Content
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.0 PHR MBTS
- Dow DOWLEX™ 2505 Linear Low Density Polyethylene, Narrow MW Distribution
- Ametek Tungsten-Copper Composites AWC 7525
Copyright © lookpolymers.com All Rights Reserved