DuPont Performance Polymers Crastin® LW9030 NC010 PBT+ASA  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® LW9030 NC010 PBT+ASA  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9030 NC010 is a 30% glass fiber reinforced polybutylene terephthalate blend for injection molding. It has improved surface aesthetics excellent dimensionalInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
1.44 g/cc
0.0520 lb/in³
ISO 1183
Water Absorption 0.72 %
<br>@Thickness 2.00 mm
 0.72 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.240 %
<br>@Thickness 2.00 mm
 0.240 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 67000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 260 °C
 67000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
77000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 250 °C
 77000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
89000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 240 °C
 89000 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
278000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 260 °C
 278000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
325000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 250 °C
 325000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
383000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 240 °C
 383000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0015 cm/cm
0.0015 in/in
48h at 80°C; ISO 294-4
0.0020 cm/cm
0.0020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
48h at 80°C; ISO 294-4
0.0070 cm/cm
0.0070 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ISO 527-1/-2
Tensile Stress 3.26 MPa
<br>@Strain 0.250 %,<br> Temperature 160 °C
 473 psi
<br>@Strain 0.250 %,<br> Temperature 320 °F
 ISO 11403-1 -2
13.4 MPa
<br>@Strain 1.50 %,<br> Temperature 160 °C
 1940 psi
<br>@Strain 1.50 %,<br> Temperature 320 °F
 ISO 11403-1 -2
17.0 MPa
<br>@Strain 3.00 %,<br> Temperature 160 °C
 2470 psi
<br>@Strain 3.00 %,<br> Temperature 320 °F
 ISO 11403-1 -2
21.8 MPa
<br>@Strain 0.250 %,<br> Temperature 40.0 °C
 3160 psi
<br>@Strain 0.250 %,<br> Temperature 104 °F
 ISO 11403-1 -2
23.9 MPa
<br>@Strain 0.250 %,<br> Temperature 23.0 °C
 3470 psi
<br>@Strain 0.250 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
25.6 MPa
<br>@Strain 0.250 %,<br> Temperature 0.000 °C
 3710 psi
<br>@Strain 0.250 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
25.9 MPa
<br>@Strain 0.250 %,<br> Temperature -20.0 °C
 3760 psi
<br>@Strain 0.250 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
27.3 MPa
<br>@Strain 0.250 %,<br> Temperature -40.0 °C
 3960 psi
<br>@Strain 0.250 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
95.9 MPa
<br>@Strain 1.50 %,<br> Temperature 40.0 °C
 13900 psi
<br>@Strain 1.50 %,<br> Temperature 104 °F
 ISO 11403-1 -2
111 MPa
<br>@Strain 1.50 %,<br> Temperature 23.0 °C
 16100 psi
<br>@Strain 1.50 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
125 MPa
<br>@Strain 1.50 %,<br> Temperature 0.000 °C
 18100 psi
<br>@Strain 1.50 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
132 MPa
<br>@Strain 1.50 %,<br> Temperature -20.0 °C
 19100 psi
<br>@Strain 1.50 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
138 MPa
<br>@Strain 1.50 %,<br> Temperature -40.0 °C
 20000 psi
<br>@Strain 1.50 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.105 %,<br> Time 3600 sec
 1450 psi
<br>@Strain 0.105 %,<br> Time 1.00 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.110 %,<br> Time 36000 sec
 1450 psi
<br>@Strain 0.110 %,<br> Time 10.0 hour
 isochronous; ISO 11403-1 -2
10.0 MPa
<br>@Strain 0.120 %,<br> Time 360000 sec
 1450 psi
<br>@Strain 0.120 %,<br> Time 100 hour
 isochronous; ISO 11403-1 -2
20.0 MPa
<br>@Strain 0.274 %,<br> Time 3.60e+6 sec
 2900 psi
<br>@Strain 0.274 %,<br> Time 1000 hour
 isochronous; ISO 11403-1 -2
50.0 MPa
<br>@Strain 0.778 %,<br> Time 3.60e+6 sec
 7250 psi
<br>@Strain 0.778 %,<br> Time 1000 hour
 isochronous; ISO 11403-1 -2
50.0 MPa
<br>@Strain 0.684 %,<br> Time 360000 sec
 7250 psi
<br>@Strain 0.684 %,<br> Time 100 hour
 isochronous; ISO 11403-1 -2
60.0 MPa
<br>@Strain 0.715 %,<br> Time 3600 sec
 8700 psi
<br>@Strain 0.715 %,<br> Time 1.00 hour
 isochronous; ISO 11403-1 -2
60.0 MPa
<br>@Strain 0.757 %,<br> Time 36000 sec
 8700 psi
<br>@Strain 0.757 %,<br> Time 10.0 hour
 isochronous; ISO 11403-1 -2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 9.50 GPa
1380 ksi
ISO 527-1/-2
1.441 GPa
<br>@Temperature 160 °C
 209.0 ksi
<br>@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
6.071 GPa
<br>@Temperature 80.0 °C
 880.5 ksi
<br>@Temperature 176 °F
 Dynamic; ISO 11403-1 -2
8.992 GPa
<br>@Temperature 30.0 °C
 1304 ksi
<br>@Temperature 86.0 °F
 Dynamic; ISO 11403-1 -2
9.489 GPa
<br>@Temperature -20.0 °C
 1376 ksi
<br>@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
9.77 GPa
<br>@Temperature -50.0 °C
 1420 ksi
<br>@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Flexural Strength 190 MPa
27600 psi
ISO 178
Flexural Modulus 8.50 GPa
1230 ksi
ISO 178
Secant Modulus 2.85 GPa
<br>@Strain 1.50 %,<br> Temperature 100 °C
 413 ksi
<br>@Strain 1.50 %,<br> Temperature 212 °F
 ISO 11403-1 -2
4.03 GPa
<br>@Strain 1.50 %,<br> Temperature 80.0 °C
 584 ksi
<br>@Strain 1.50 %,<br> Temperature 176 °F
 ISO 11403-1 -2
4.40 GPa
<br>@Strain 0.250 %,<br> Temperature 100 °C
 638 ksi
<br>@Strain 0.250 %,<br> Temperature 212 °F
 ISO 11403-1 -2
6.04 GPa
<br>@Strain 0.250 %,<br> Temperature 80.0 °C
 876 ksi
<br>@Strain 0.250 %,<br> Temperature 176 °F
 ISO 11403-1 -2
6.39 GPa
<br>@Strain 1.50 %,<br> Temperature 40.0 °C
 927 ksi
<br>@Strain 1.50 %,<br> Temperature 104 °F
 ISO 11403-1 -2
7.40 GPa
<br>@Strain 1.50 %,<br> Temperature 23.0 °C
 1070 ksi
<br>@Strain 1.50 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
8.33 GPa
<br>@Strain 1.50 %,<br> Temperature 0.000 °C
 1210 ksi
<br>@Strain 1.50 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
8.72 GPa
<br>@Strain 0.250 %,<br> Temperature 40.0 °C
 1260 ksi
<br>@Strain 0.250 %,<br> Temperature 104 °F
 ISO 11403-1 -2
8.80 GPa
<br>@Strain 1.50 %,<br> Temperature -20.0 °C
 1280 ksi
<br>@Strain 1.50 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
9.20 GPa
<br>@Strain 1.50 %,<br> Temperature -40.0 °C
 1330 ksi
<br>@Strain 1.50 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
9.56 GPa
<br>@Strain 0.250 %,<br> Temperature 23.0 °C
 1390 ksi
<br>@Strain 0.250 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
10.24 GPa
<br>@Strain 0.250 %,<br> Temperature 0.000 °C
 1485 ksi
<br>@Strain 0.250 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
10.36 GPa
<br>@Strain 0.250 %,<br> Temperature -20.0 °C
 1503 ksi
<br>@Strain 0.250 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
10.92 GPa
<br>@Strain 0.250 %,<br> Temperature -40.0 °C
 1584 ksi
<br>@Strain 0.250 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
8.00 kJ/m²
<br>@Temperature -30.0 °C
 3.81 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
ISO 180/1U
50.0 kJ/m²
<br>@Temperature -30.0 °C
 23.8 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 180/1U
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/1eU
6.50 J/cm²
<br>@Temperature -30.0 °C
 30.9 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 179/1eU