SABIC Innovative Plastics NORYL V095 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL V095 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
83dc HDT, V0@1.5mm,Higher flow version of PX1007
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 250 °C |
30 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 20 % | 20 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.60e+17 ohm-cm | 1.60e+17 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.64 @Frequency 1.00e+6 Hz |
2.64 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 2.65 @Frequency 50.0 - 60.0 Hz |
2.65 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 27.0 kV/mm @Thickness 1.60 mm |
686 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0050 @Frequency 50.0 - 60.0 Hz |
0.0050 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- SABIC BM1052 High Density Polyethylene for Blow Molding
- Stellarchem LP-845 TPE Compound
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
- Loctite® 243 Oil Resistant/Medium Strength Threadlocker
- Eagle Brass 230 Red Brass, Spring
- E-Polymers TEKANATE® G7020 General Purpose Easy Molding Polycarbonate
- 3M 7046 Screen Printable Vinyl Performance Label Products
- Akro-Plastic Akromid® A3 GF 50 (2423) PA 6.6 Conditioned, 50% Glass Filled
- LTL Color Compounds ColorFast® FRPS200 Styrene, High Impact
Copyright © lookpolymers.com All Rights Reserved