Techmer ES Luriblend® PA6 TSX10 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6 TSX10 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant (10%)Features: Lubricated and Good Wear ResistanceInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Water Absorption | 1.1 % @Time 86400 sec |
1.1 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 3.17 mm |
0.014 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Yield | 22 % | 22 % | ASTM D638 |
| Flexural Yield Strength | 97.9 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.23 | 0.23 | ASTM D1894 |
| Coefficient of Friction, Static | 0.18 | 0.18 | ASTM D1894 |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 93.6 µm/m-°C | 52.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 °C | 340 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Shinkong Synthetic Fibers Shinite® F202G30 PBT, 30% Glass Filled, Fire Retardant, Halogen Free
- SABIC Innovative Plastics LNP THERMOCOMP DB008ERP PC (Asia Pacific)
- A. Schulman POLYBATCH™ Weatherwood 60190U Concentrate Based In LLDPE
- TIMCAL TIMREX® MK25 Primary Synthetic Graphite
- Hexcel® HexForce™ 6557 Fiber Glass Fabric
- Trelleborg Emerson & Cuming Stycast® E 1420FR Two-Component Epoxy Flame Retardant Encapsulant
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-550 (FEF)
- 3M Scotchcal™ ElectroCut™ 7125-197 Graphic Film
- Lubrizol Estane® 2103-90AENH Film Grade Thermoplastic Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved