- SABIC Innovative Plastics NORYL PX1391 PPE+PS
SABIC Innovative Plastics NORYL PX1391 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX1391 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. Unfilled. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.44 GPa | 354 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 2.24 J/cm | 4.20 ft-lb/in | ASTM D256 |
| 1.33 J/cm @Temperature -40.0 °C |
2.49 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature 0.000 - 100 °C |
38.0 µin/in-°F @Temperature 32.0 - 212 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C @Thickness 6.40 mm |
320 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 153 °C @Thickness 6.40 mm |
307 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.67 @Frequency 1.00e+6 Hz |
2.67 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.3 kV/mm @Thickness 1.60 mm |
490 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 1.00e+6 Hz |
0.00050 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- ExxonMobil LL 1002.32 Blown Film Resin (discontinued **)
- SABIC Innovative Plastics Lexan® FXE101R PC
- Mitsubishi Xantar® 27 SR FD Polycarbonate
- LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced
- SABIC Innovative Plastics Xenoy® X4810 PBT+PC (Asia Pacific)
- DSM Akulon® K224-G6-FC BK00001 PA6-GF30
- Clariant Renol BR7039 Nylon 6 Alloy, bondable to TPU
- 3M W-610 Ceramic Microspheres
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 60% Cold Rolled (UNS S30400)
- DuPont Performance Polymers Hytrel® 5526 TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved