SABIC Innovative Plastics NORYL PX1265 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX1265 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive applications. Exterior mirror and cluster housings, speaker grilles, cowl tops, exterior trim. 270F (132C) DTUL.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 35 % | 35 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 2.45 J/cm | 4.59 ft-lb/in | ASTM D256 |
| 1.33 J/cm @Temperature -40.0 °C |
2.49 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature 0.000 - 100 °C |
40.0 µin/in-°F @Temperature 32.0 - 212 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C @Thickness 6.40 mm |
275 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Gwent Electronic Materials C2050712D58 Silver Ink for ITO Substrates
- Gwent Electronic Materials C2090512D1 70:30 Silver Palladium Ink
- Huntsman AVALON® 65 AE Thermoplastic Polyurethane
- Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled
- Solvay TECHNYL® A 216 PA66, DRY
- UBE UBEPOL BR150L Non-Oil Extended Synthetic Rubber (Raw Polymer)
- Eurostar Star L PA6 30V D61 PA6, Glass Filled, Injection Molding
- Azoty Tarnow™ TARNOFORM 300 GF6 BK POM
- 3M 7049 Screen Printable Extended Life Vinyl Performance Label Products
- Lehmann & Voss PLASLUBE NY-1/SI/2/NT Polyamide 66, lubricant modified
Copyright © lookpolymers.com All Rights Reserved