SABIC Innovative Plastics NORYL IGN5531 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL IGN5531 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl IGN5531 may be an excellent material candidate for ignition coils and other application requiring electrically insulating properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.060 % | 0.060 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.4 g/10 min @Load 5.00 kg, Temperature 300 °C |
6.4 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 5.0 g/10 min @Load 5.00 kg, Temperature 300 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 5 mm/min; ASTM D638 |
| 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.10 GPa | 740 ksi | 5 mm/min; ASTM D638 |
| 5.80 GPa | 841 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 135 MPa | 19600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 140 MPa | 20300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.50 GPa | 653 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| 0.800 J/cm @Temperature -30.0 °C |
1.50 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 28.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 82.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 82.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 158 °C | 316 °F | Rate B/50; ASTM D1525 |
| 158 °C | 316 °F | Rate B/50; ISO 306 | |
| 159 °C | 318 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Polymer Resources NY6-G43 Nylon 6, 43% Glass Reinforced
- Hybrid Plastics Nanoreinforced® POSS® 5% POSS-polyimide
- Inno-Comp INNOPOL® CS 1-3120 B DEL 20% Talc Filled Polypropylene Homopolymer
- Michelman® Nomar® 70AFN Non-abrasive paper coating
- Schott OG570 Long Pass Filter
- Special Metals NILOMAG® Alloy 77
- A. Schulman POLYBATCH™ Red 5500 Concentrate Based In Polyethylene
- 3M 7733FLW Overlaminating Film
- Fainplast Compounds AP 90/2 Flexible PVC, Flame Retardant Insulation
- Karina E 843-18/302-CRM Gray PVC Compound
Copyright © lookpolymers.com All Rights Reserved