Iran Petrochemical (PCC) EX 2 S HF 7750 M2 High Density Polyethylene

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , HDPE, Fiber Grade
Manufacturer	Iran Petrochemical Commercial Co. (PCC)
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Iran Petrochemical (PCC) EX 2 S HF 7750 M2 High Density Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

EX2S is a high density polyethylene with 1-Butene as co monomer. It is medium molar mass, low density grade with a narrow molar mass distribution, high rigidity, good tear strength. Applications: monofilaments, ropes, yarns, netting geotextiles & cavil engineering.Information provided by Iran Petrochemical Commercial Co.

Physical Properties	Metric	English	Comments
Density	0.956 g/cc	0.0345 lb/inÂ³	ISO 1183
Melt Flow	3.3 g/10 min @Load 5.00 kg, Temperature 190 Â°C	3.3 g/10 min @Load 11.0 lb, Temperature 374 Â°F	ISO 1133
	33 g/10 min @Load 21.6 kg, Temperature 190 Â°C	33 g/10 min @Load 47.6 lb, Temperature 374 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	62	62	ISO 868
Tensile Stress	31.0 MPa	4500 psi	at Break; ISO 527
Tensile Strength, Yield	27.0 MPa	3920 psi	ISO 527
Elongation at Break	>= 1000 %	>= 1000 %	ISO 527
Elongation at Yield	10 %	10 %	ISO 527
Tensile Modulus	1.20 GPa	174 ksi	ISO 527
Charpy Impact, Notched	2.30 J/cmÂ²	10.9 ft-lb/inÂ²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Softening Point	80.0 Â°C	176 Â°F	ISO 306
Brittleness Temperature	>= -80.0 Â°C	>= -112 Â°F	ASTM D746-72

Processing Properties	Metric	English	Comments
Melt Temperature	220 - 270 Â°C	428 - 518 Â°F

Descriptive Properties	Value	Comments
Flexural Creep Modulus (MPa)	1350	4 point, 1 min; DIN 19537-2