SABIC Innovative Plastics NORYL N1150 PPE+PS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL N1150 PPE+PS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* N1150 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and good flow, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating at 0.75 mm with a specific density of 1.11 g/cm^3. Noryl* 1150 may be an excellent material candidate for applications requiring electrically insulating properties, low moisture absorption, low warpage, and thin wall flame resistance.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Water Absorption at Saturation 0.070 %
0.070 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 280 °C
15 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 15 g/10 min

@Load 5.00 kg,
Temperature 280 °C
15 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 52.0 MPa
7540 psi
50 mm/min; ISO 527
55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 72.0 MPa
10400 psi
50 mm/min; ISO 527
75.0 MPa
10900 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 7.0 %
7.0 %
50 mm/min; ISO 527
8.0 %
8.0 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527
4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.65 GPa
384 ksi
1 mm/min; ISO 527
2.70 GPa
392 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 105 MPa
15200 psi
2 mm/min; ISO 178
117 MPa
17000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.60 GPa
377 ksi
2 mm/min; ISO 178
3.05 GPa
442 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
0.650 J/cm

@Temperature -30.0 °C
1.22 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 40.0 J

@Temperature 23.0 °C
29.5 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 54.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
54.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 57.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
57.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 109 °C
228 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
108 °C

@Thickness 3.20 mm
226 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 130 °C
266 °F
Rate B/50; ASTM D1525
130 °C
266 °F
Rate B/50; ISO 306
132 °C
270 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
UL 94