SABIC Innovative Plastics NORYL GTX GTX8120P PPE+PA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX8120P PPE+PA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GTX8120P is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaks
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.00 % | 1.00 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 2.5 % | 2.5 % | ISO 62 |
| Melt Index of Compound | 4.0 g/10 min @Load 10.0 kg, Temperature 280 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.80 GPa | 986 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
41.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Vicat Softening Point | 235 °C | 455 °F | Rate B/50; ISO 306 |
| 235 °C | 455 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Nye Lubricants 167B (SO) Synthetic Oil
- Renegade Materials Corporation RM-3010 Bismaleimide (BMI) Resin for VARTM
- LG Chemical LG401 Styrene-Butadiene-Styrene
- Greene Tweed CHEMRAZ® 555 Perfluoroelastomer
- Samsung Cheil Industries Starex® WX-9300 ASA, Unreinforced Heat Resistant
- CeramTec Sonox® P6 Piezoceramic
- Trelleborg Commercial Neoprene® C801 Chloroprene
- DuPont Performance Polymers Zytel® 70G13HS1L NC010 Nylon 66 (Unverified Data**)
- C.O.I.M. LARIPUR® LPR9025 Special Adipate Ester Polyurethane
- Momentive Performance Materials PolarTherm® PTX25 Boron Nitride (BN) Powder
Copyright © lookpolymers.com All Rights Reserved