Ineos ABS Lustran® M202AS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Ineos ABS
Trade Name Lustran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® M202AS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Grade for self coloring, optimized base color, easy flowing, contains antistatic additives. ,Property data per ISO test methods.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Melt Flow 34 g/10 min

@Load 10.0 kg,
Temperature 220 °C
34 g/10 min

@Load 22.0 lb,
Temperature 428 °F
Estimated using room temperature density
Mechanical Properties Metric English Comments
Tensile Strength, Yield 44.0 MPa
6380 psi
Elongation at Yield 2.4 %
2.4 %
Tensile Modulus 2.30 GPa
334 ksi
Charpy Impact Unnotched 10.0 J/cm²
47.6 ft-lb/in²
8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 0.900 µm/m-°C

@Temperature 20.0 °C
0.500 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
Vicat Softening Point 100 °C
212 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
Dielectric Strength 36.0 kV/mm
914 kV/in
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
0.0080

@Frequency 1e+6 Hz
0.0080

@Frequency 1e+6 Hz
Comparative Tracking Index 600 V
600 V