SABIC Innovative Plastics NORYL EN265 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL EN265 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion grade. 254F (123C) DTUL. UL94 V-1 rated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 99.0 MPa | 14400 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.86 J/cm | 3.48 ft-lb/in | ASTM D256 |
| 1.33 J/cm @Temperature -40.0 °C |
2.49 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Gardner Impact | 4.00 J @Temperature -40.0 °C |
2.95 ft-lb @Temperature -40.0 °F |
ASTM D3029 |
| 14.0 J @Temperature -30.0 °C |
10.3 ft-lb @Temperature -22.0 °F |
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.49 mm |
V-1 @Thickness 0.0587 in |
UL 94 |
| V-0 @Thickness 5.99 mm |
V-0 @Thickness 0.236 in |
UL 94 | |
| Oxygen Index | 29.2 % | 29.2 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.69 @Frequency 50.0 - 60.0 Hz |
2.69 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 19.6 kV/mm @Thickness 3.20 mm |
498 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.00070 @Frequency 50.0 - 60.0 Hz |
0.00070 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Radiant Panel Listing | RP100 | UL Tested |
| UV-light, water exposure/immersion | F1 | UL 746C |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 15 HI PA6, 15% glass fibre, improved strength
- Nilit FRIANYL B63 H-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
- Formosa Plastics Formolene® LH5240 Injection Molding HDPE (discontinued **)
- Covestro Apec® DP 1-9349/5 Polycarbonate (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP JF004P PES (Asia Pacific)
- A. Schulman POLYFORT™ FPP 1285U Glass Filled, UV Stable Impact Copolymer Polypropylene
- Zeon Chemicals HyTemp® AR74 AR Polyacrylate Elastomer
- Fainplast Compounds AP 80 Flexible PVC, Flame Retardant Insulation
Copyright © lookpolymers.com All Rights Reserved