SABIC Innovative Plastics Lexan® OQ1060 PC Copolymer
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® OQ1060 PC Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Optical quality, high flow, high purity Polycarbonate copolymer resin with reduced oxygen transmission for advanced DVD applications such as Limited Play DVD.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Oxygen Transmission | <= 59.1 cc-mm/m²-24hr-atm | <= 150 cc-mil/100 in²-24hr-atm | - |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 42 g/10 min @Load 1.20 kg, Temperature 300 °C |
42 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 44 g/10 min @Load 1.20 kg, Temperature 300 °C |
44 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 110 MPa | 16000 psi | ISO 2039-1 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D 638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D 638 |
| 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | >= 25 % | >= 25 % | 50 mm/min; ISO 527 |
| 50 % | 50 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 |
| 7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| 2.55 GPa | 370 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| 2.51 GPa | 364 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.100 J/cm @Temperature 23.0 °C |
0.187 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 2.00 kJ/m² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 72.0 J @Temperature 23.0 °C |
53.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 73.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
40.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 73.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
40.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ASTM D 1525 |
| 140 °C | 284 °F | Rate B/50; ISO 306 | |
| 141 °C | 286 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D 542 |
Users viewing this material also viewed the following:
- Resinlab® EP1290 Clear Mineral Filled Epoxy Adhesive
- LyondellBasell PM Propylene glycol methyl ether
- Indium Corp. Indalloy® 244 99.3Sn/0.7Cu Lead-Free Solder Alloy
- SABIC Innovative Plastics NORYL V0150B PPE+HIPS (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRICOMP SFL36 PA12 (Europe-Africa-Middle East)
- SABIC Innovative Plastics ULTEM CRS5211R PEI
- Styrolution Terlux® 2812 HD MABS
- Covestro Baydur® STR/C-400 BB Polyurethane Composite SRIM Foam, 60% Glass Filled, MDI-based 2-Component Liquid System
- Alliance N-38H Neodymium Iron Boron Magnetic Material
Copyright © lookpolymers.com All Rights Reserved