SABIC Innovative Plastics Lexan® ML3286 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® ML3286 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LEXAN ML3286 is a 17% glass reinforced grade for use in less demanding applications.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.12 %
0.12 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.30 %

@Temperature 23.0 °C
 0.30 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
on tensile bar; SABIC Method
Melt Flow 5.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 5.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
5 mm/min; ISO 527
Elongation at Break 5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 4.00 GPa
580 ksi
1 mm/min; ISO 527
Flexural Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
Flexural Modulus 4.50 GPa
653 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
6.00 kJ/m²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
30.0 kJ/m²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
3.50 J/cm²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 UL 94 by SABIC-IP
Glow Wire Test 850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 50.0 - 60.0 Hz
 3.0

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
 406 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
 0.0010

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.010

@Frequency 1.00e+6 Hz
 0.010

@Frequency 1.00e+6 Hz
 IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2