SABIC Innovative Plastics Lexan® FXE1112T PC Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXE1112T PC Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan* FXE1112T Lexan* polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. Lexan FXE1112T resin may be an excellent candidate for a broad range of applications. This product is available in GE Plastics' Visual fX* Piano Black, Raven Black & Illuminate color range only.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.090 % | 0.090 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.24 % @Temperature 23.0 °C |
0.24 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 19 g/10 min @Load 1.20 kg, Temperature 300 °C |
19 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 117.9 % | 117.9 % | Type I, 50 mm/min; ASTM D 638 |
| 119.4 % | 119.4 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.4 % | 5.4 % | 50 mm/min; ISO 527 |
| 5.7 % | 5.7 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.26 GPa | 328 ksi | 50 mm/min; ASTM D 638 |
| 2.34 GPa | 339 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ISO 178 |
| 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.14 GPa | 310 ksi | 2 mm/min; ISO 178 |
| 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 6.18 J/cm @Temperature -30.0 °C |
11.6 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 7.36 J/cm @Temperature 23.0 °C |
13.8 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 65.0 kJ/m² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 74.0 J @Temperature 23.0 °C |
54.6 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.8 µm/m-°C @Temperature -40.0 - 95.0 °C |
41.6 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 74.8 µm/m-°C @Temperature 23.0 - 80.0 °C |
41.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 76.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
42.4 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 76.4 µm/m-°C @Temperature 23.0 - 80.0 °C |
42.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 138 °C | 280 °F | Rate A/50; ASTM D 1525 |
| 138 °C | 280 °F | Rate B/50; ISO 306 | |
| 139 °C | 282 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed the following:
- Omnia Plastica Omniamid PA6 GHR HR - Dry
- Overview of materials for Phenolic; Unreinforced; Molded
- Lavergne VYPET VNT 630 FR PET 30% Glass Reinforced, Flame Retardant
- Styron CALIBREâ„¢ 303-10 Polycarbonate Resin
- Hexcel® HexForce™ 7580 Fiber Glass Fabric
- Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb
- Aaron Industries AAROLENE® ARPP H 200-1 Polypropylene Compounded Resin
- 3M 365 Thermosetable Glass Cloth Tape
- Polymer Resources PPX-SF1 Modified PPO, Structural Foam Grade, Easy Flow (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved