Lanxess Durethan® BC 700 HTS 900116 Nylon 6/66 (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BC 700 HTS 900116 Nylon 6/66
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6/66
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.027 g/cc | 1.027 g/cc | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527-1,-2 |
| Elongation at Yield | 6.5 % | 6.5 % | ISO 527-1,-2 |
| Tensile Modulus | 0.210 GPa | 30.5 ksi | Conditioned; ISO 527-1,-2 |
| 0.980 GPa | 142 ksi | ISO 527-1,-2 | |
| Flexural Strength | 12.0 MPa @Strain 9.00 % |
1740 psi @Strain 9.00 % |
Conditioned; ISO 178 |
| 35.0 MPa @Strain 6.10 % |
5080 psi @Strain 6.10 % |
ISO 178 | |
| Flexural Yield Strength | 7.00 MPa @Strain 3.50 % |
1020 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 30.0 MPa @Strain 3.50 % |
4350 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 0.230 GPa | 33.4 ksi | Conditioned; ISO 178 |
| 0.980 GPa | 142 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 85.0 kJ/m² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180-1U |
| Charpy Impact, Notched | 10.5 J/cm² @Temperature -30.0 °C |
50.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 200 µm/m-°C | 111 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 200 µm/m-°C | 111 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 211 °C | 412 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 53.0 °C | 127 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 280 °C | 446 - 536 °F | Recommended |
| 270 °C | 518 °F | Processing conditions for test specimens; ISO 294 | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Recommended |
| 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.00 - 0.060 % | 0.00 - 0.060 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6/66-HI,BHS,14-010 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® C7-4535 DICUP R Dow-Corning Biomedical Grade ETR Elastomer
- Ineos ABS Centrex® 821 ASA Blend (discontinued **)
- Mueller Ecostreamâ„¢ GreenDropâ„¢ C27450 Lead Free Plumbing Brass
- Techmer ES HiFill® PA6 CF30 30% Carbon Fiber Filled
- DSM Arnitel® PM471 Polyether Ester Elastomer (European and Asian Grade)
- Elastocon TPE Technologies Elastocon® SMR1555 Thermoplastic Polyolefin Elastomer
- Bulk Molding Compounds BMC 610 Mineral filled, glass-fiber-reinforced polyester compound
- Ashley Polymers Ashlene® D925LH-30G Nylon 12, 30% Glass Reinforced, Lubricated
- Polimeri Europa Extir® D 5000 AE Expandable Polystyrene - Flame Retardant
Copyright © lookpolymers.com All Rights Reserved