LATI Latimass 37 B01-01 D025 Bio-Polymer

Category	Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer	LATI
Trade Name	Latimass
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latimass 37 B01-01 D025 Bio-Polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Specific density compound based on Bio-Polymer (PLA, PHB, ...). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	2.47 g/cc	0.0892 lb/in³
Linear Mold Shrinkage, Flow	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in
Linear Mold Shrinkage, Transverse	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	40.0 MPa	5800 psi
Elongation at Break	0.50 %	0.50 %
Tensile Modulus	8.10 GPa	1170 ksi
Charpy Impact Unnotched	0.500 J/cm²	2.38 ft-lb/in²
Charpy Impact, Notched	0.100 J/cm²	0.476 ft-lb/in²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	55.0 °C	131 °F
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F
Vicat Softening Point	60.0 °C @Load 5.00 kg	140 °F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	180 - 200 °C	356 - 392 °F
Mold Temperature	15.0 - 30.0 °C	59.0 - 86.0 °F
Drying Temperature	40.0 - 50.0 °C @Time 21600 sec	104 - 122 °F @Time 6.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa