SABIC Innovative Plastics LNP VERTON RV00CEXS PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV00CEXS PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RV00CEXS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.72 g/cc | 1.72 g/cc | ASTM D792 |
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.530 % | 0.530 % | 50% RH, 24 hrs; ASTM D570 |
| 0.670 % | 0.670 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 254 MPa | 36800 psi | Type I, 5 mm/min; ASTM D638 |
| 264 MPa | 38300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 |
| 1.6 % | 1.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 21.86 GPa | 3171 ksi | 1 mm/min; ISO 527 |
| 22.08 GPa | 3202 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 403 MPa | 58500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 404 MPa | 58600 psi | ISO 178 | |
| Flexural Yield Strength | 404 MPa | 58600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 18.1 GPa | 2630 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 18.74 GPa | 2718 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 4.10 J/cm | 7.68 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.7 J/cm | 21.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 62.0 kJ/m² | 29.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 49.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 248 °C @Thickness 3.20 mm |
478 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® XHT4141 PC Copolymer (Asia Pacific)
- Abatron AboCast 8-23/Abocure 8-23 Epoxy (discontinued **)
- Kinetics MIM F1537 (ASTM F1537) HIP and Heat Treat
- Momentive Performance Materials TUFELâ„¢ II 94405 Low Volatile Extrusion Heat Cured Rubber
- A. Schulman POLYBATCH™ 7171 POLYBATCH® Concentrate Based In Polyethylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR DBPH-50
- 3M FM095 Indoor UL Recognized Matte Silver Polyester Label Product
- Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound (discontinued **)
- Chesterton KPC 820 Industrial Degreaser
Copyright © lookpolymers.com All Rights Reserved