SABIC Innovative Plastics LNP VERTON RV00AXX9 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV00AXX9 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RV00AXX9 is a compound based on PA 66 resin containing Long Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.800 % | 0.800 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0024 cm/cm @Time 86400 sec |
0.0024 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0079 cm/cm @Time 86400 sec |
0.0079 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 268 MPa | 38900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 17.6 GPa | 2550 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 405 MPa | 58700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 15.5 GPa | 2250 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² | 47.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
30.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 262 °C | 504 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- Mo-Sci Corporation GL-0252 Blue Soda-Lime Glass Spheres
- Shin-Etsu Silicones LIMSâ„¢ KE2095-40AB Elastomer
- Universal Wire Works 4130 Steel Welding Wire
- Trelleborg E569 EPDM Rubber
- ChevronTexaco ISO 32 AIO
- DuPont Performance Polymers Crastin® S600LF NC010 PBT
- Colorite Polymers Vinylbond 6527P-MD Grey 499 Compound
- Chevron Phillips Marlex® 9519H High Density Polyethylene, Blow Molding
- Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel
- 3M FM692 Indoor UL Recognized Computer Imprintable Clear Polyester Label Product
Copyright © lookpolymers.com All Rights Reserved