LG Chemical LUPOY GP-2400 General Purpose Modified PC, 40% Glass Fiber Reinforced, High Strength
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 40% Glass Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP-2400 General Purpose Modified PC, 40% Glass Fiber Reinforced, High Strength.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive front ends, cluster pad main panel (instrument panel), lower cluster pad main, console box, glove box cover, door, wheel cover and cap, defroster grill, back mirror housingElectrical and Electronic: Monitor housing, fax housing, notebook PC housing, cellular phone case, fax and copy machine frame, CD ROM drive tray and main frame, relay case, connector, switchIndustrial Parts and Household Appliance: Helmet, terminal box, electrical tool housing, industrial bobbin, distributing board box, power tool component, gears and cams, water meter housingInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 167 MPa | 24200 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 185 MPa | 26800 psi | ASTM D790 |
| Flexural Modulus | 9.31 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Temperature 23.0 °C |
2.38 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 270 - 300 °C | 518 - 572 °F | |
| Middle Barrel Temperature | 280 - 315 °C | 536 - 599 °F | |
| Front Barrel Temperature | 290 - 330 °C | 554 - 626 °F | |
| Nozzle Temperature | 290 - 330 °C | 554 - 626 °F | |
| Melt Temperature | 300 - 340 °C | 572 - 644 °F | |
| Mold Temperature | 80.0 - 115 °C | 176 - 239 °F | |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Parker Chomerics THERM-A-FORM T647 Cure-in-Place Potting and Underfill Material
- LG Chemical TR-557I Transparent ABS, High Impact, Ice Colored Pellets
- Huntsman Matrimid 5292A Resin
- KKPC KOSYN 1502W Styrene Butadiene Rubber
- Teknor Apex APEX® 3700-65 Polyvinyl Chloride, Flexible
- Samsung Cheil Industries Starex® SF-0950S MABS, Unreinforced Scratch Resistant
- A. Schulman POLYFORT™ PP 3720
- Eastman Tenite Propionate 381E4000015 Clear, Trsp Cellulose Acetate Propionate
- Eurostar Starflam PFB139E PA6, Glass Fiber/Bead Filled, Flame Retardant, Injection Molded
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Hi-Sil 233 Filler
Copyright © lookpolymers.com All Rights Reserved