LG Chemical Lupox® HI2152 PBT+GF15%
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® HI2152 PBT+GF15%.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+GF15%, High ImpactApplication: IT/OA, E&E (Bobbin, Switch)CAS No. 9003-01-04, 65997-17-3, 24968-12-5 and 103598-77-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.011 cm/cm @Thickness 3.20 mm |
0.0070 - 0.011 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 83.4 MPa @Thickness 3.20 mm |
12100 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm |
3.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 123 MPa @Thickness 3.20 mm |
17800 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 4.12 GPa @Thickness 3.20 mm |
597 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.539 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.01 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C @Thickness 6.40 mm |
387 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Nozzle Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Melt Temperature | 245 - 255 °C | 473 - 491 °F | Injection Molding |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Network Polymers NPP 20-1001
- DuPont Performance Polymers Zytel® HTN 52G45HSL BK083 Polyphthalamide (PPA) (Unverified Data**)
- Magyar Aluminum ALOLT 720 Aluminum Hydroxide
- Indium Corp. Indalloy 123 Tin Solder Alloy
- Samsung Cheil Industries Starex® ES-0173 ABS, Extrusion Grade
- Cytec (Conap) RN-1000 / EA-028 Conapoxy® Resin / Conacure® Hardener
- Chosun Refractories A18H Magnesia Carbon Bricks for Electric Arc Furnace
- ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, 1149°C (2100°F) Solution Treated, UNS N06601
- 3M FM018 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- E-Polymers EFLEX® V2060 SEBS/TPV
Copyright © lookpolymers.com All Rights Reserved