SABIC Innovative Plastics LNP Thermocomp WC003P Polyester Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp WC003P Polyester Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* WC003P is a compound based on Polyester resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
1.38 g/cc
0.0499 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.080 %
0.080 %
23°C / 50% RH; ISO 62
0.050 %

@Time 86400 sec
 0.050 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
SABIC Method
0.0050 - 0.0070 cm/cm

@Time 86400 sec
 0.0050 - 0.0070 in/in

@Time 24.0 hour
 ASTM D 955
0.0050 - 0.0070 cm/cm

@Time 86400 sec
 0.0050 - 0.0070 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.011 - 0.013 cm/cm
0.011 - 0.013 in/in
SABIC Method
0.011 - 0.013 cm/cm

@Time 86400 sec
 0.011 - 0.013 in/in

@Time 24.0 hour
 ASTM D 955
0.011 - 0.013 cm/cm

@Time 86400 sec
 0.011 - 0.013 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 104 MPa
15100 psi
ASTM D 638
104 MPa
15100 psi
ISO 527
Elongation at Break 1.9 %
1.9 %
ISO 527
2.0 %
2.0 %
ASTM D 638
Tensile Modulus 10.0 GPa
1450 ksi
1 mm/min; ISO 527
10.47 GPa
1519 ksi
50 mm/min; ASTM D 638
Flexural Strength 151 MPa
21900 psi
ASTM D 790
157 MPa
22800 psi
ISO 178
Flexural Modulus 8.68 GPa
1260 ksi
ASTM D 790
9.03 GPa
1310 ksi
ISO 178
Izod Impact, Notched 0.320 J/cm

@Temperature 23.0 °C
 0.599 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 4.80 J/cm

@Temperature 23.0 °C
 8.99 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature 23.0 °C
 1.43 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 29.0 kJ/m²

@Temperature 23.0 °C
 13.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
7.00 J

@Temperature 23.0 °C
 5.16 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 24.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
25.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 14.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 74.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
 41.5 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
193 °C

@Thickness 3.20 mm
 379 °F

@Thickness 0.126 in
 unannealed; ASTM D 648