- Clariant Renol PPA1100G60 Polyphthalamide, 60% Glass Fiber
Clariant Renol PPA1100G60 Polyphthalamide, 60% Glass Fiber
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PPA1100G60 Polyphthalamide, 60% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | ASTM D792 |
| Filler Content | 60 % | 60 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 255 MPa | 37000 psi | ASTM D638 |
| Elongation at Break | 1.0 - 2.0 % | 1.0 - 2.0 % | ASTM D638 |
| Flexural Yield Strength | 345 MPa | 50000 psi | ASTM D790 |
| Flexural Modulus | 20.7 GPa | 3000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Temperature 22.8 °C |
2.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 282 °C | 540 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 302 - 329 °C | 575 - 625 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Dry Time | 6 hour @Temperature 79.4 °C |
6 hour @Temperature 175 °F |
to ensure moisture content is less than 0.05% |
| Injection Pressure | 41.4 - 74.5 MPa | 6000 - 10800 psi | Secondary |
| 68.9 - 124 MPa | 10000 - 18000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Polykemi AB POLYshine PBT D231 GF15 PBT, Glass-Fiber Reinforced
- Ravago Manufacturing Americas Hysun™ A3525 ASA+PC
- Resinlab® CYNERGY CA6001 Adhesive
- Spartech PP5230 Calcium Carbonate Filled Homopolymer
- Stir SpA A 58 AT (PVC)
- Lubrizol Estane® X-585A-31 Thermoplastic Polyurethane
- CTC SunPro® SP 200 P3081 Polypropylene Copolymer
- Axiall 22880 Coax & Telecom Flexible PVC
- Arlon 30580R020 0.020" (0.508 mm) Uncured Unsupported Silicone Rubber on Kodacel Carrier
- Parker Chomerics CHO-BOND 1073, Part B Conductive Powder
Copyright © lookpolymers.com All Rights Reserved