- SABIC Innovative Plastics LNP Thermocomp PF00A PA 6 (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP Thermocomp PF00A PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp PF00A PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% glass fibre reinforced Polyamide 6 injection moulding resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.60 % | 0.60 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.5 % @Temperature 23.0 °C |
4.5 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | on tensile bar; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | on tensile bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ISO 2039-2 |
| Tensile Strength at Break | 224 MPa | 32500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 320 MPa | 46400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 13.25 GPa | 1922 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature -40.0 °C |
6.66 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 16.0 kJ/m² @Temperature -20.0 °C |
7.61 ft-lb/in² @Temperature -4.00 °F |
80*10*4; ISO 180/1A | |
| 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| 90.0 kJ/m² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
6.67 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
46.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 215 °C | 419 °F | Rate B/120; ISO 306 |
| 218 °C | 424 °F | Rate B/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 by SABIC-IP |
| Oxygen Index | 25 % | 25 % | LOI; ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.6 @Frequency 50.0 - 60.0 Hz |
3.6 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0061 @Frequency 50.0 - 60.0 Hz |
0.0061 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | >= 350 V | >= 350 V | IEC 60112 |
| 500 V | 500 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA-924 Impact Modified Acrylic Resin
- Nylene® Vexel™ B12GF45 SA , 45% Glass Reinforced PBT
- Solvay Specialty Polymers Amodel® AFA-6145 V0 Z Polyphthalamide (PPA) (Unverified Data**)
- BASF Capron® 8232G 25% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Ineos ABS Lustran® PG 298
- Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F)
- Solvay Specialty Polymers Amodel® A-1130 FW Polyphthalamide (PPA), 30% Glass Fiber
- DuPont™ Nomex® E56 Paper, 5 mil Nominal Thickness
- 3M 1450 General Purpose Aluminum Foil Tape
- A. Schulman ComAlloy Hiloy® 273 Polystyrene Alloy, Glass Reinforced, Flow Enhanced