Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer S&E Specialty Polymers
Trade Name TufTech™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF S&E Specialty Polymers TufTech™ SE11-023E PVC Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Application: Automotive – PVC, black, exterior weatherable, elastomeric, extrusion molding compound.Information provided by S&E Specialty Polymers
Physical Properties Metric English Comments
Specific Gravity <= 1.22 g/cc
<= 1.22 g/cc
ISO 1183
Mechanical Properties Metric English Comments
Hardness, Shore A 58.63 - 69.29

@Temperature 85.0 °C,
Time 605000 sec
 58.63 - 69.29

@Temperature 185 °F,
Time 168 hour
 Heat Aging; ISO 188, Method B
55.0 - 65.0

@Time 15.0 sec
 55.0 - 65.0

@Time 0.00417 hour
 ISO 868
Tensile Strength at Break 13.0 MPa
1890 psi
500mm/min; ISO 527, 1A
13.4741 MPa

@Temperature 85.0 °C,
Time 605000 sec
 1954.26 psi

@Temperature 185 °F,
Time 168 hour
 Heat Aging; ISO 188, Method B
Elongation at Break 385 %
385 %
500mm/min; ISO 527, 1A
393.9 %

@Treatment Temp. 85.0 °C,
Time 605000 sec
 393.9 %

@Treatment Temp. 185 °F,
Time 168 hour
 Heat Aging; ISO 188, Method B
Tear Strength >= 33.0 kN/m
>= 188 pli
Method B, angle die, 500mm/min.; ISO 34-1
Compression Set 25.0 %

@Temperature 24.0 °C,
Time 259000 sec
 25.0 %

@Temperature 75.2 °F,
Time 72.0 hour
 ISO 815-1, Type A
57.0 %

@Temperature 70.0 °C,
Time 79200 sec
 57.0 %

@Temperature 158 °F,
Time 22.0 hour
 ISO 815-1, Type A
Descriptive Properties Value Comments
Cold Flex -34°C
SAE J323, Method A, No cracks