SABIC Innovative Plastics LNP LUBRICOMP UX05051 PPA (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP UX05051 PPA (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Internally lubricated Polyphthalamide compound, containing Glass Fiber and PTFE. Added features include Heat Stabilized, Flame Retardant and Hot Water Moldable
Physical Properties Metric English Comments
Density 1.76 g/cc
0.0636 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 138 MPa
20000 psi
5 mm/min; ISO 527
Elongation at Break 1.0 %
1.0 %
5 mm/min; ISO 527
Tensile Modulus 12.1 GPa
1750 ksi
1 mm/min; ISO 527
Flexural Yield Strength 188 MPa
27300 psi
2 mm/min; ISO 178
Flexural Modulus 10.7 GPa
1550 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 11.1 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 52.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 28.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 273 °C
523 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 UL 94