Cossa Polimeri ESTADIENE 0420 HHT Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTADIENE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTADIENE 0420 HHT Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS for injection molding or extrusionVery high thermal resistance, good impact resistanceInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ASTM D 638 |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | ASTM D 638 |
| Elongation at Break | 10 % | 10 % | ASTM D 638 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.50 J/cm @Temperature 0.000 °C |
2.81 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 2.00 J/cm @Temperature 23.0 °C |
3.75 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 115 °C @Load 5.00 kg |
239 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 125 °C @Load 0.999 kg |
257 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- RheTech Products G13P100-332UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, (GM 9772) Light Neutral
- Pyrotek Pyrocast 80 Lightweight Castable Refractory
- Lehmann & Voss LUVOCOM® 1-1119 VP Polyamide 66, with carbon fiber, heat stabilized
- SABIC Innovative Plastics LNP THERMOCOMP EF004 PEI
- A. Schulman POLYFORT™ FPP 3715 Glass Filled Homopolymer Polypropylene
- Dow Corning 832 MULTI-SURFACE ADHESIVE SEALANT
- Dalau Dalcon 018 85% Virgin PTFE, 15% Graphite
- Bulk Molding Compounds BMC 851 Corrosion Resistant, Flame Retardant Molding Compound
- E-Polymers EFLEX® S5050 Extrusion
Copyright © lookpolymers.com All Rights Reserved