- Industeel SIRIUS 310 25% Cr - 0.6% Si Heat Resistant Stainless Steel
Industeel SIRIUS 310 25% Cr - 0.6% Si Heat Resistant Stainless Steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | SIRIUS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel SIRIUS 310 25% Cr - 0.6% Si Heat Resistant Stainless Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: CLI SIRIUS 310 grade is a fully austenitic stainless steel containing 25% Cr, 0.6% Si and 20% Ni additions. The alloy is well known for its multi-purpose high temperature corrosion resistance behavior. Carbon additions are optimized in order to provide improved creep resistance properties. Alloy CLI SIRIUS 310 can be easily welded. The alloy is designed for high temperature applications up to 1100°C (2012°F) in oxidizing atmospheres. The alloy can be also used in slightly oxidizing atmospheres,, nitriding, cementing, sulphurising conditions as well as with thermal cyclings, but the maximum temperature of use will be reduced.Information provided by manufacturer.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 550 MPa | 79800 psi | Typical after Solution Annealing |
| Tensile Strength, Yield | 245 MPa @Strain 0.200 % |
35500 psi @Strain 0.200 % |
Typical after Solution Annealing |
| 265 MPa @Strain 1.00 % |
38400 psi @Strain 1.00 % |
Typical after Solution Annealing | |
| Elongation at Break | 45 % | 45 % | Typical |
| Creep Strength | 120 MPa @Temperature 600 °C, Time 3.60e+6 sec |
17400 psi @Temperature 1110 °F, Time 1000 hour |
|
| Modulus of Elasticity | 200 GPa | 29000 ksi | |
| Poissons Ratio | 0.333 | 0.333 | Calculated |
| Shear Modulus | 75.0 GPa @Temperature 20.0 °C |
10900 ksi @Temperature 68.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.5 µm/m-°C @Temperature 20.0 - 100 °C |
8.61 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 16.0 µm/m-°C @Temperature 20.0 - 200 °C |
8.89 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 17.0 µm/m-°C @Temperature 20.0 - 400 °C |
9.44 µin/in-°F @Temperature 68.0 - 752 °F |
||
| 18.0 µm/m-°C @Temperature 20.0 - 600 °C |
10.0 µin/in-°F @Temperature 68.0 - 1110 °F |
||
| Specific Heat Capacity | 0.480 J/g-°C @Temperature 20.0 °C |
0.115 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 14.0 W/m-K @Temperature 20.0 °C |
97.2 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Chromium, Cr | 25 % | 25 % | |
| Iron, Fe | 54.3 - 54.4 % | 54.3 - 54.4 % | As remainder |
| Nickel, Ni | 20 % | 20 % | |
| Silicon, Si | 0.60 % | 0.60 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000900 ohm-cm @Temperature 20.0 °C |
0.0000900 ohm-cm @Temperature 68.0 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® PC0700 PC (Europe-Africa-Middle East)
- SABIC R40039E Medium Density Polyethylene for Rotational Molding
- Lehmann & Voss LUVOCOM® 2607-7921 Blend based on polyaryl ether ketone, unreinforced
- Lord Adhesives 7542E Two-Component Urethane Adhesive
- Karina E 813-35/1-DY-SN-ERYB Compound PVC Ivory
- Saint-Gobain Rulon® II Bearing/Seal PTFE
- ELASTO UK Dryflex® 420451S SBS Based Material, 45D Hardness, Natural
- CMW® D56 Silver Nickel Contact Material B693
- ExxonMobil Santoprene® 181-55MED Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved