Iran Petrochemical (PCC) 2101TN47 Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) 2101TN47 Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDPE 2101TN47 Shrink FilmThis grade enables high speed production of film without blocking.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ISO R527-1 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO R527-1 |
| Film Elongation at Break, MD | >= 200 % | >= 200 % | ISO R527-1 |
| Film Elongation at Break, TD | >= 500 % | >= 500 % | ISO R527-1 |
| Modulus of Elasticity | 0.160 GPa | 23.2 ksi | MD; ISO R527-1 |
| 0.170 GPa | 24.7 ksi | TD; ISO R527-1 | |
| Tensile Impact | 300 J/cm | 562 ft-lb/in | ASTM D4272 |
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 |
| Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 |
| 40.0 kN/m | 228 pli | MD; ISO 6383-2 | |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO R527-1 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ISO R527-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 11 % | 11 % | ASTM D1003A |
| Gloss | 49 % | 49 % | ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clarity, mV | 37 | Sabtec |
Users viewing this material also viewed the following:
- Mytex Polymers AN16L(W)-D56 Polypropylene, Talc filled, Compounded, Elastomer, Impact modified
- Plaskolite West Optix® CA-927 G HF Clear Impact Modified Acrylic Resin
- Global MPP-140-C 40% Mica Reinforced Polypropylene
- SYNTHOS Kralex® 1723 Styrene Butadiene Rubber
- SABIC Innovative Plastics LNP THERMOCOMP BFL2200 PC (Asia Pacific)
- Solvay GEROPON® CYA/75 Surfactant
- A. Schulman PP 2268-01 Polypropylene High Flow, Impact Copolymer Polypropylene
- Covestro Makrolon® 2467 Polycarbonate
- EMS-Grivory Grivory® L 20A Z PA12
- China Tungsten YG6X Tungsten Carbide for Cutting Tools
Copyright © lookpolymers.com All Rights Reserved