- Styron EMERGEâ„¢ 8600-10 Polycarbonate
Styron EMERGEâ„¢ 8600-10 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 8600-10 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ PC 8600-10 is a translucent, ignition-resistant polycarbonate resin. The resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It is an easy flow PC resin suitable for use in injection molded applications in the computer, electronics, electrical, and information technology equipment markets.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Ultimate | 57.9 MPa | 8400 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 2in/min, 0.125 in specimen, injection molded, unannealed; ASTM D638 |
| Elongation at Break | 110 % | 110 % | 0.125 in, injection molded, unannealed; ASTM D638 |
| Elongation at Yield | 6.2 % | 6.2 % | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Modulus | 2.21 GPa | 320 ksi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Flexural Strength | 93.8 MPa | 13600 psi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 59.0 J | 43.5 ft-lb | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 64.8 µm/m-°C @Temperature 20.0 °C |
36.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
| Vicat Softening Point | 149 °C | 300 °F | 120°C/hr, 10N; ASTM D1525 |
| UL RTI, Electrical | 125 °C | 257 °F | UL 746 |
| UL RTI, Mechanical with Impact | 125 °C | 257 °F | UL 746 |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| Oxygen Index | 35 % | 35 % | ASTM D2863 |
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 125 °C | 257 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- Reltek BONDiT™ B-46TH Adhesive and Sealant
- PolyOne Geon™ Vinyl Flexible XV3900 Polyvinyl Chloride, Flexible (PVC, Flexible)
- ExxonMobil Escorene® LL-8556 LLDPE, Rotational Molding Powder (discontinued **)
- Kennametal Stellite Stellite® 3 PM cast
- IDI Composites E-203 Thermoset Polyester, Sheet
- LG Chemical LUPOY GN5001RFH PC/ABS, Halogen Free Flame Retardant, Heat Resistance
- Lord Adhesives 7544 Two-Component, Non-Sag, Fast-Cure Urethane Adhesive
- Solvay Specialty Polymers Ajedium™ Films -- Radel® R-5100 NT15 Polyphenylsulfone (PPSU)
- ELASTO UK Dryflex® 650800 TPE, Improved Compression Set and High Temperature Resistance, 80A Hardness
- ExxonMobil Teresstic 68
Copyright © lookpolymers.com All Rights Reserved