- SABIC Innovative Plastics LNP THERMOTUF VF1001S Super Tough Nylon
SABIC Innovative Plastics LNP THERMOTUF VF1001S Super Tough Nylon
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF VF1001S Super Tough Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* VF1001S is a Super Tough Nylon containing glass fiber. Characteristics of this grade is Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.680 % | 0.680 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 |
| 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
| 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 7.6 % | 7.6 % | 5 mm/min; ISO 527 |
| 9.3 % | 9.3 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.4 % | 3.4 % | Type I, 5 mm/min; ASTM D638 |
| 3.4 % | 3.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.29 GPa | 477 ksi | 1 mm/min; ISO 527 |
| 3.39 GPa | 492 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 86.0 MPa | 12500 psi | ISO 178 |
| Flexural Modulus | 2.76 GPa | 400 ksi | 2 mm/min; ISO 178 |
| 2.94 GPa | 426 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.20 J/cm | 13.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 11.0 J | 8.11 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.7 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 97.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
54.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 242 °C | 468 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 249 °C @Thickness 3.20 mm |
480 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 309 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 198 °C @Thickness 3.20 mm |
388 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers CPE-01-266A-405 Black PVC
- Sumitomo Chemical ESPOLEX® 3785 Thermoplastic Elastomer
- Polyram PlusTek PA801 Nylon 6.6 Copolymer for Injection Molding, Impact Modified
- Voloknohim Filament Nylon Linear Density 93.5 tex
- ExxonMobil HDPE HTA 108 High Density Polyethylene Resin
- Chicago Extruded Metals BioBrass® UNS C62300 Aluminum Bronze
- Aaron Industries AAROPRENE® CFIPP 2020 High Impact Calcium Carbonate Filled Polypropylene
- Asia International Enterprise (Hong Kong) 60T6 Nylon 66, 30% Filled
Copyright © lookpolymers.com All Rights Reserved