SABIC Innovative Plastics LNP THERMOTUF VF006U Super Tough Nylon
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF VF006U Super Tough Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* VF006U is a compound based on Super Tough Nylon containing Glass Fiber. Characteristics of this grade are High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.500 % | 0.500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.720 % | 0.720 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
| 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 7.65 GPa | 1110 ksi | 1 mm/min; ISO 527 |
| 7.78 GPa | 1130 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 114 MPa | 16500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 131 MPa | 19000 psi | ISO 178 | |
| Flexural Yield Strength | 119 MPa | 17300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.14 GPa | 891 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.74 GPa | 978 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.830 J/cm | 1.55 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.33 J/cm | 9.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 99.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
55.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 237 °C | 459 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 235 °C @Thickness 3.20 mm |
455 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nabaltec APYRAL® 16 Al(OH)3
- Plastcom SLOVASTER® B1 GF 6 HML PBT, 6% glass fibre
- SABIC Innovative Plastics Cycoloy® CE3210 PC+ABS (Europe-Africa-Middle East)
- Karina E 20/15-RG-GE Cream Color Concentrate for PVC
- Huntsman AVALON® 90 ABR Thermoplastic Polyurethane
- SK Chemicals SKYTHANE® S395A Polyester Based Thermoplastic Polyurethane Elastomer
- Borealis Bormed™ HF855MO Polypropylene Homopolymer for Medical Applications
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 82A
- ExxonMobil Santoprene® 211-55 Thermoplastic Elastomer (discontinued **)
- Premix Premi-Glas® 1200-24 Polyester SMC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved