- Lehmann & Voss LUVOCOM® 1100-8401 Polyether sulfone, unreinforced
Lehmann & Voss LUVOCOM® 1100-8401 Polyether sulfone, unreinforced
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1100-8401 Polyether sulfone, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Superheated steam sterilizable.Inherent flame resistance.High quality terminal bar, switches and plugs, relais, lamp reflectors, sterilizable medical equipment.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.17 g/cc | 2.17 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |
| Melt Flow | 21.7 g/10 min @Load 5.00 kg, Temperature 345 °C |
21.7 g/10 min @Load 11.0 lb, Temperature 653 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 80.0 MPa | 11600 psi | |
| Elongation at Yield | 2.8 % | 2.8 % | |
| 3.3 % | 3.3 % | flexural | |
| Modulus of Elasticity | 5.50 GPa | 798 ksi | |
| Flexural Strength | 115 MPa | 16700 psi | |
| Flexural Modulus | 4.50 GPa | 653 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| 220 °C | 428 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | |
| Vicat Softening Point | 215 °C | 419 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 340 - 360 °C | 644 - 680 °F | |
| Zone 1 | 355 - 375 °C | 671 - 707 °F | |
| Zone 2 | 360 - 380 °C | 680 - 716 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 200 °C | 248 - 392 °F | |
| Drying Temperature | 150 °C @Time 10800 - 18000 sec |
302 °F @Time 3.00 - 5.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Quadrant EPP Ertalyte® PET-P, Polyester-semi-crystalline thermoplastic, extruded (ASTM Product Data Sheet)
- Pasargad Polymer Peyvand Pasalen 3P-H3520B Polypropylene, 20% EPDM Filled
- Huntsman IROGRAN® A 75 P 4655 N TPU-Polyester
- Momentive Performance Materials UltraSpan® Weatherstrip
- SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer
- Tra-Con Tra-Bond F113SC BLK High Tg Fiber Optic Epoxy Adhesive
- Aremco Aremco-Bond™ 568 High Performance Epoxide
- ACC Silcoset 101 Low Tear Condensation Cure 2-Part Molding Rubber
- Cos40 Cork/Neoprene Rubber Sheet
Copyright © lookpolymers.com All Rights Reserved