SABIC Innovative Plastics LNP THERMOTUF OF006I PPS - Linear
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF OF006I PPS - Linear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* OF006I is a compound based on PPS - Linear resin containing Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| 1.486 g/cc | 0.05369 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0400 % | 0.0400 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0023 cm/cm @Time 86400 sec |
0.0023 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm @Time 86400 sec |
0.0067 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 139 MPa | 20200 psi | ISO 527 |
| 143 MPa | 20700 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.4 % | 2.4 % | ASTM D638 | |
| Tensile Modulus | 9.82 GPa | 1420 ksi | 1 mm/min; ISO 527 |
| 10.82 GPa | 1569 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| 212 MPa | 30700 psi | ISO 178 | |
| Flexural Modulus | 9.79 GPa | 1420 ksi | ASTM D790 |
| 10.06 GPa | 1459 ksi | ISO 178 | |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.79 J/cm | 14.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
Users viewing this material also viewed the following:
- Polykemi AB POLYabs SS0 GK10 ABS, High Flow
- Radici Radilon® S 35FL (cond.) Nylon 6
- Plastcom SLOVAMID 6 MI PA6, improved strength
- Huntsman IROGRAN® A 85 P 4666 Ether-Based TPU-For Cable Industry
- Teknor Apex APEX® 65008 Polyvinyl Chloride, Flexible
- Master Bond EP21LV-LO Two Component, Lower Viscosity, Room Temperature Curing Epoxy System
- A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene
- Covestro Desmopan® DP 8798A Polyurethane
- Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (1 mm Molded Thickness)
- Ceradyne Ceralloy® 1370-1E Aluminum Nitride
Copyright © lookpolymers.com All Rights Reserved