SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
1.30 g/cc
0.0470 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0028 cm/cm

@Time 86400 sec
 0.0028 in/in

@Time 24.0 hour
 ISO 294
0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0049 cm/cm

@Time 86400 sec
 0.0049 in/in

@Time 24.0 hour
 ISO 294
0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 84.0 MPa
12200 psi
ISO 527
88.0 MPa
12800 psi
ASTM D638
Tensile Strength, Yield 84.0 MPa
12200 psi
ISO 527
88.0 MPa
12800 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ISO 527
1.7 %
1.7 %
ASTM D638
Elongation at Yield 1.6 %
1.6 %
ISO 527
1.7 %
1.7 %
ASTM D638
Tensile Modulus 6.83 GPa
991 ksi
1 mm/min; ISO 527
6.89 GPa
999 ksi
50 mm/min; ASTM D638
Flexural Strength 118 MPa
17100 psi
ISO 178
241 MPa
35000 psi
ASTM D790
Flexural Modulus 6.60 GPa
957 ksi
ISO 178
12.41 GPa
1800 ksi
ASTM D790
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.16 J/cm
7.79 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 14.0 J
10.3 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 57.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 32.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
58.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 32.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 39.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
39.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 22.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 111 °C
232 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
110 °C

@Thickness 3.20 mm
 230 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
219 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
102 °C

@Thickness 3.20 mm
 216 °F

@Thickness 0.126 in
 unannealed; ASTM D648