Total Lumicene® mPE M 3410 EP HDPE Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer Total Atofina
Trade Name Lumicene® mPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Lumicene® mPE M 3410 EP HDPE Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Outstanding clarity and gloss; excellent bubble stability; excellent tear strength; high puncture resistance; good stiffness; excellent heat sealing properties; excellent compatibility with LDPE and LLDPE.Applications: Lumicene® mPE M 2710 EP is recommended for clarity shrink films, food packaging, laminations and multilayer packaging film.Information provided provided by Total Petrochemicals.
Physical Properties Metric English Comments
Density 0.927 g/cc
0.0335 lb/in³
ASTM D792
Water Vapor Transmission 13.9 g/m²/day

@Thickness 0.0254 mm
0.895 g/100 in²/day

@Thickness 0.00100 in
Thickness 25.4 microns
1.00 mil
as tested; BUR 2.5
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.90 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
High Load Melt Index 30 g/10 min

@Load 21.6 kg,
Temperature 190 °C
30 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 580 %

@Thickness 0.0254 mm
580 %

@Thickness 0.00100 in
ASTM D882A
Film Elongation at Break, TD 720 %

@Thickness 0.0254 mm
720 %

@Thickness 0.00100 in
ASTM D882A
Flexural Modulus 0.600 GPa
87.0 ksi
ASTM D 790
Elmendorf Tear Strength MD 165 g

@Thickness 0.0254 mm
165 g

@Thickness 0.00100 in
ASTM D1922
Elmendorf Tear Strength TD 500 g

@Thickness 0.0254 mm
500 g

@Thickness 0.00100 in
ASTM D1922
Dart Drop 5.91 g/micron

@Thickness 0.0254 mm
150 g/mil

@Thickness 0.00100 in
ASTM D1709A
Dart Drop Test 150 g
0.331 lb
1.0 mil; ASTM D 1709
Film Tensile Strength at Break, MD 33.8 MPa

@Thickness 0.0254 mm
4900 psi

@Thickness 0.00100 in
ASTM D882A
Film Tensile Strength at Break, TD 33.1 MPa

@Thickness 0.0254 mm
4800 psi

@Thickness 0.00100 in
ASTM D882A
1% Secant Modulus, MD 214 MPa

@Thickness 0.0254 mm
31000 psi

@Thickness 0.00100 in
ASTM D882A
1% Secant Modulus, TD 172 MPa

@Thickness 0.0254 mm
25000 psi

@Thickness 0.00100 in
ASTM D882A
Thermal Properties Metric English Comments
Melting Point 121 °C
250 °F
ASTM D3417
Descriptive Properties Value Comments
Process Film
Region US & Canada
Bamberger Polymers Distribution