- SABIC Innovative Plastics LNP THERMOCOMP RX99732C PA 66
SABIC Innovative Plastics LNP THERMOCOMP RX99732C PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX99732C PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* PDX-R-99732 is a Nylon 6/6 with proprietary fillers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.590 % | 0.590 % | 50% RH, 24 hrs; ASTM D570 |
| 0.810 % | 0.810 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 186 MPa | 27000 psi | Type I, 5 mm/min; ASTM D638 |
| 186 MPa | 27000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 186 MPa | 27000 psi | Type I, 5 mm/min; ASTM D638 |
| 186 MPa | 27000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 14.01 GPa | 2032 ksi | 1 mm/min; ISO 527 |
| 15.18 GPa | 2202 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 250 MPa | 36300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 253 MPa | 36700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.2 GPa | 1480 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.83 GPa | 1571 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.45 J/cm | 2.72 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.9 J/cm | 24.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 74.0 kJ/m² | 35.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
28.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 234 °C | 453 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 234 °C @Thickness 3.20 mm |
453 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PEAK Werkstoff DISPAL S260 Aluminum Alloy, AlSi25Cu4Mg, Condition F
- LyondellBasell Pro-fax PD702NW Polypropylene Homopolymer, Nucleated/Antistat
- GrafTech GRAFOIL® GHN Standard Fluid Sealing Laminate, Non-Metal Reinforced
- LATI Latistat 67-08 PA66, Impact Modified
- Techmer ES Luriblend® PSU GF20 TL5 20% Glass Filled
- ExxonMobil Escorene™ FL 00014 Ethylene Vinyl Acetate Copolymer (European Grade)
- Fainplast Compounds FKA 0753 Flexible PVC, Flame Retardant Insulation Lead Free
- Clariant Renol PPOSP0001 Polyphenylene Oxide, Mineral Filled
- Abatron AboCast 8103-27 High-Performance Dielectric Epoxy
Copyright © lookpolymers.com All Rights Reserved