Overview of materials for Phenolic, Resole, Wood Filled

Category Polymer , Thermoset , Phenolic , Phenolic, Resole, Wood Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Phenolic, Resole, Wood Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Wood Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.36 - 1.54 g/cc
0.0491 - 0.0556 lb/in³
Average value: 1.43 g/cc Grade Count:10
Water Absorption 0.360 - 0.630 %
0.360 - 0.630 %
Average value: 0.484 % Grade Count:10
Linear Mold Shrinkage 0.00233 - 0.0101 cm/cm
0.00233 - 0.0101 in/in
Average value: 0.00554 cm/cm Grade Count:10
Mechanical Properties Metric English Comments
Hardness, Rockwell E 57.0 - 89.0
57.0 - 89.0
Average value: 75.3 Grade Count:10
Tensile Strength, Ultimate 51.0 - 69.0 MPa
7400 - 10000 psi
Average value: 58.0 MPa Grade Count:10
Elongation at Break 0.680 - 1.26 %
0.680 - 1.26 %
Average value: 0.927 % Grade Count:10
Modulus of Elasticity 6.60 - 9.40 GPa
957 - 1360 ksi
Average value: 8.03 GPa Grade Count:10
Flexural Yield Strength 74.0 - 105 MPa
10700 - 15200 psi
Average value: 85.4 MPa Grade Count:10
Flexural Modulus 6.60 - 8.60 GPa
957 - 1250 ksi
Average value: 7.50 GPa Grade Count:10
Compressive Yield Strength 157 - 215 MPa
22800 - 31200 psi
Average value: 189 MPa Grade Count:10
Poissons Ratio 0.330 - 0.360
0.330 - 0.360
Average value: 0.346 Grade Count:5
Shear Modulus 2.70 - 3.26 GPa
392 - 473 ksi
Average value: 2.96 GPa Grade Count:5
Izod Impact, Notched 0.152 - 0.209 J/cm
0.285 - 0.392 ft-lb/in
Average value: 0.183 J/cm Grade Count:10
Charpy Impact, Notched 0.182 - 0.220 J/cm²
0.866 - 1.05 ft-lb/in²
Average value: 0.194 J/cm² Grade Count:10
Thermal Properties Metric English Comments
CTE, linear 37.0 - 67.0 µm/m-°C

@Temperature 40.0 - 130 °C
20.6 - 37.2 µin/in-°F

@Temperature 104 - 266 °F
Average value: 56.6 µm/m-°C Grade Count:7
Thermal Conductivity 0.370 - 0.460 W/m-K

@Temperature 100 - 100 °C
2.57 - 3.19 BTU-in/hr-ft²-°F

@Temperature 212 - 212 °F
Average value: 0.400 W/m-K Grade Count:4
Maximum Service Temperature, Air 183 - 207 °C
361 - 405 °F
Average value: 196 °C Grade Count:10
Deflection Temperature at 1.8 MPa (264 psi) 158 - 225 °C
316 - 437 °F
Average value: 186 °C Grade Count:10
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:10
Oxygen Index 25.5 - 31.0 %
25.5 - 31.0 %
Average value: 28.3 % Grade Count:4
Electrical Properties Metric English Comments
Electrical Resistivity 8.30e+11 - 3.00e+13 ohm-cm
8.30e+11 - 3.00e+13 ohm-cm
Average value: 1.04e+13 ohm-cm Grade Count:9
Dielectric Constant 4.40 - 7.00
4.40 - 7.00
Average value: 5.74 Grade Count:9
Dielectric Strength 8.00 - 14.2 kV/mm
203 - 361 kV/in
Average value: 11.2 kV/mm Grade Count:9
Dissipation Factor 0.0410 - 0.172
0.0410 - 0.172
Average value: 0.0658 Grade Count:9
Arc Resistance 87.0 - 183 sec
87.0 - 183 sec
Average value: 144 sec Grade Count:9
Comparative Tracking Index 175 V
175 V
Average value: 175 V Grade Count:10