- Honeywell ACLAR® 11A (8.00 mil) CTFE Homopolymer, Barrier Film (discontinued **)
Honeywell ACLAR® 11A (8.00 mil) CTFE Homopolymer, Barrier Film (discontinued **)
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® 11A (8.00 mil) CTFE Homopolymer, Barrier Film
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ACLAR® 11A is a CTFE homopolymer, high performance barrier film for industrial and electronics applications.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.11 g/cc | 2.11 g/cc | ASTM D1505 |
| Density | 2.13 g/cc | 0.0770 lb/in³ | Yield Density |
| Water Vapor Transmission | 0.0300 g/m²/day | 0.00193 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 |
| Thickness | 203 microns | 8.00 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 150 - 225 % | 150 - 225 % | ASTM D882 |
| Film Elongation at Break, TD | 175 - 250 % | 175 - 250 % | ASTM D882 |
| Secant Modulus, MD | 1.207 - 1.551 GPa | 175.1 - 225.0 ksi | ASTM D882 |
| Secant Modulus, TD | 1.207 - 1.551 GPa | 175.1 - 225.0 ksi | ASTM D882 |
| Tear Strength Test | 450 - 525 | 450 - 525 | graves tear MD, grams/mil; ASTM D1004 |
| 450 - 525 | 450 - 525 | graves tear TD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 34.5 - 41.4 MPa | 5000 - 6000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.5 - 41.4 MPa | 5000 - 6000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.209 W/m-K | 1.45 BTU-in/hr-ft²-°F | |
| Melting Point | 211 °C | 412 °F | crystalline melting point; ASTM D4591 |
| Oxygen Index | 100 % | 100 % | ASTM D2863 |
| Shrinkage, MD | <= 2.0 % | <= 2.0 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= 2.0 % | <= 2.0 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | non flammable |
Users viewing this material also viewed the following:
- Network Polymers NPP 808 C5WW
- PSM Industries PolyAlloys MIM-2700 sintered Low Alloy Steel
- SABIC Innovative Plastics LNP LUBRILOY UX99725 PPA
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66
- Unitika FUN-8000
- Huntsman Rexell® V8401 Cast Film Extrusion LLDPE (discontinued **)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N774 (SRF) Filler
- Weartech International WT-12H Cobalt Hardfacing & Wear Resistant Alloy
Copyright © lookpolymers.com All Rights Reserved