SABIC Innovative Plastics LNP THERMOCOMP RF003H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF003H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF003H is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Moisture Absorption | 1.10 % | 1.10 % | 50% RH, 24 hrs; ASTM D570 |
| 1.60 % | 1.60 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.12 GPa | 743 ksi | 5 mm/min; ASTM D638 |
| 5.16 GPa | 748 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 156 MPa | 22600 psi | ISO 178 |
| 171 MPa | 24800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.95 GPa | 573 ksi | 2 mm/min; ISO 178 |
| 4.51 GPa | 654 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.570 J/cm | 1.07 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.37 J/cm | 8.19 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 256 °C @Thickness 3.20 mm |
493 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 240 °C @Thickness 3.20 mm |
464 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- LG Chemical LUPOL HG-3200 High Gloss Polypropylene, 20% Mineral Fillers
- LG Chemical LUPOY GN1006FL PC, Halogen Free, Flame Retardant, Transparency
- Gouda Vuurvast AK 85 KP Dense Refractory Brick
- A. Schulman POLYBATCH™ White P8555 SD Concentrate Based In Homopolymer Polypropylene
- Hexcel® Redux® 312UL Modified epoxy film adhesive
- Enviro Tech International EnSolv® n-Propyl Bromide Vapor Degreasing Solvent
- 3M 1267 EMI Shielding Tape
- Nye Lubricants 782D-G4 (NG) Synthetic Oil
- Fainplast Compounds PH 62 Flexible PVC, Transparent Extrusion
- Polymer Resources PPX-SF1 Modified PPO, Structural Foam Grade, Easy Flow (Unverified Data**)